Problem & Lösung

Q

Pulsating Droplets at the Die Exit

A

This problem is a typical manifestation of pulsating droplets at the die exit in extrusion molding. The core of the solution lies in eliminating the root cause of the defect through systematic optimization of process parameters (temperature, speed, pressure) and precision correction of the die/si...

Extrusion & Post pulsating droplets at the die exittemperature

Q

Spiral Marks on the Inner Wall of Pipes

A

This problem is a typical manifestation of spiral marks on the inner wall of pipes in extrusion molding. The core of the solution lies in eliminating the root cause of the defect through systematic optimization of process parameters (temperature, speed, pressure) and precision correction of the d...

Extrusion & Post spiral marks on the inner wall of pipes

Q

Anisotropic Thermal Expansion of Products

A

This problem is a typical manifestation of anisotropic thermal expansion of products in compression molding. The core of the solution lies in the reasonable preheating of the material and the guarantee of fluidity, as well as the precise matching of mold temperature and molding pressure. It is re...

Extrusion & Post shrinkage ratewall thickness designcooling water channelsholding pressuredimensional accuracy

Q

Internal delamination of the product

A

This problem is a typical manifestation of internal delamination of the product in compression molding, and the core of the solution lies in the reasonable preheating of the material and the guarantee of flowability, as well as the precise matching of mold temperature and molding pressure. It is ...

Extrusion & Post internal delamination of the product temperature pressure mold

Q

Thermal shock cracks caused by opening the furnace too quickly after sintering is completed

A

The essence of cracking is that the internal stress exceeds the strength limit of the material, and it is necessary to proceed from two aspects: reducing stress concentration and improving material toughness.

Extrusion & Post PTFE cracking caused by opening the furnace too quickly after sintering is completed thermal shock

Q

Elastic recovery cracks appear in the PTFE preform

A

The essence of cracking is that the internal stress exceeds the strength limit of the material, and it is necessary to proceed from two aspects: reducing stress concentration and improving material toughness.

Extrusion & Post PTFE demolding preforming rebound powder

Q

Cooling cracks generated inside the product

A

The essence of cracking is that the internal stress exceeds the strength limit of the material, and it is necessary to proceed from two aspects: reducing stress concentration and improving material toughness.

Extrusion & Post cooling rate PTFE cooling cracks generated inside the product

Q

Blank delamination during cold-press preforming

A

The essence of the interlayer separation problem is insufficient interfacial bonding force, which needs to be systematically improved from three aspects: impregnation quality, interlayer cleanliness, and process parameters.

Extrusion & Post demolding preforming powder holding pressure cold pressing

Q

Product delamination

A

The essence of the interlayer separation problem is insufficient interfacial bonding force, which needs to be systematically improved from three aspects: impregnation quality, interlayer cleanliness, and process parameters.

Extrusion & Post preforming density isostatic pressing

Q

Poor interlayer compatibility of different resin batches

A

This problem requires comprehensive analysis from multiple dimensions of materials, processes, equipment, and operation, and should be solved by systematically optimizing process parameters and the quality control system.

Extrusion & Post poor interlayer compatibility of different resin batches process optimization