Insufficient Breaking Strength of Polypropylene PP Fiber

Insufficient PP fiber strength is caused by improper raw material selection or process parameters, and needs to be optimized from the material grade and drawing conditions.

Extrusion & Post fiber strengthPP fiberspinning temperaturedraw ratioside air blowing

9 görüntüleme

Tam Yanıtı Oku →

Die Head Pressure Fluctuation of Polypropylene Extruder

Die head pressure fluctuation is caused by unstable discharge or filtration system problems; the extrusion parameters need to be stabilized and the filtration system maintained.

Extrusion & Post pressure fluctuationfilter screendie head temperaturebreaker plateuniform discharge

9 görüntüleme

Tam Yanıtı Oku →

Haul-Off Speed Mismatch of Polypropylene Extruded Products

Haul-off speed mismatch needs to be solved by precisely adjusting the haul-off parameters and ensuring haul-off stability.

Extrusion & Post haul-off speedspeed matchinghaul-off slippingclamping forcehaul-off control

9 görüntüleme

Tam Yanıtı Oku →

Poor Printability of Polypropylene Film

Poor printability is caused by low surface energy, and the ink adhesion needs to be improved by increasing the surface tension through corona treatment.

Extrusion & Post printabilitysurface energycorona treatmentink adhesionsurface tension

9 görüntüleme

Tam Yanıtı Oku →

Longitudinal Reversion of Polypropylene Pipe Exceeding the Standard

Excessive reversion is caused by large internal stress or excessive orientation, and needs to be solved from temperature control, cooling rate, and haul-off speed.

Extrusion & Post longitudinal reversioninternal stresscooling ratehaul-off speedmolecular orientation

9 görüntüleme

Tam Yanıtı Oku →

Unstable Discharge/Surging in Polypropylene Extrusion Process

Unstable discharge is caused by unstable solid conveying, and the barrel temperature and feeding system need to be optimized.

Extrusion & Post unstable dischargesurgingsolid conveyinghopper bridgingscrew speed

9 görüntüleme

Tam Yanıtı Oku →

Dimensional Fluctuation of Polypropylene Extruded Products

Dimensional fluctuation is caused by unstable extrusion or haul-off, and all process parameters need to be systematically stabilized.

Extrusion & Post dimensional fluctuationscrew speedhaul-off speedtemperature stabilityuniform feeding

9 görüntüleme

Tam Yanıtı Oku →

Cyclic Pressure Fatigue Failure of Polypropylene PPR Pipe

Fatigue failure is caused by internal defects and stress concentration, and needs to be improved from three aspects: pipe inner wall quality, welding quality, and material toughness.

Extrusion & Post fatigue failurePPRstress concentrationinner wall qualitywelding bead

9 görüntüleme

Tam Yanıtı Oku →

Thermal Aging Performance of Polypropylene PPR Pipe Not Up to Standard

Thermal aging performance not up to standard is caused by an insufficient antioxidant system, and needs to be solved from formulation and processing temperature control.

Extrusion & Post thermal agingantioxidantPPRoxidation induction timeextrusion temperature

9 görüntüleme

Tam Yanıtı Oku →

Melt Flow Rate Mismatch of Raw Material for Polypropylene Extrusion

MFR mismatch needs to be solved by selecting a suitable grade and adjusting the temperature parameters.

Extrusion & Post melt flow rategrade selectionextrusion gradeprocess adjustmentbatch inspection

9 görüntüleme

Tam Yanıtı Oku →