Yaygın plastik malzeme zorluklarına pratik yanıtlar

Makalelere Göz At →
2239 soru
Q
POE extrusion pelletizing strand sticking
A
Strand sticking is caused by elastic recovery and low-temperature pelletizing; high-temperature water cutting and fast cutting are the key
Extrusion & Post POE pelletizingstrand stickingpelletizing water temperaturecutter speedelastic recovery
1 görüntüleme
Tam Yanıtı Oku →
Q
POE extrusion melt fracture
Q
Microwave continuous vulcanization
A
Microwave
Extrusion & Post EPDMmicrowave
1 görüntüleme
Tam Yanıtı Oku →
Q
Large extrusion die swell
A
Die swell design compensation
Extrusion & Post EPDMdie swell
1 görüntüleme
Tam Yanıtı Oku →
Q
LCP product surface peeling and delamination
A
LCP delamination is a fragile manifestation of high anisotropy.
Extrusion & Post LCPdelaminationskin layerorientationmold temperature
1 görüntüleme
Tam Yanıtı Oku →
Q
Problem of decreased transparency of Slip Masterbatch in cast film
A
The key to slip masterbatch lies in the migration/precipitation balance.
Extrusion & Post slip masterbatchdecreased transparencycast filmmigrationCOF
1 görüntüleme
Tam Yanıtı Oku →
Q
Problem of opening sticking of Slip Masterbatch in cast film
A
The key to slip masterbatch lies in the migration/precipitation balance.
Extrusion & Post slip masterbatchopening stickingcast filmmigrationCOF
1 görüntüleme
Tam Yanıtı Oku →
Q
Problem of white powder precipitation of Slip Masterbatch in cast film
A
The key to slip masterbatch lies in the migration/precipitation balance.
Extrusion & Post slip masterbatchwhite powder precipitationcast filmmigrationCOF
1 görüntüleme
Tam Yanıtı Oku →
Q
Problem of high COF of Slip Masterbatch in cast film
A
The key to slip masterbatch lies in the migration/precipitation balance.
Extrusion & Post slip masterbatchhigh COFcast filmmigrationCOF
1 görüntüleme
Tam Yanıtı Oku →
Q
Problem of insufficient slip of Slip Masterbatch in PE blown film
A
The key to slip masterbatch lies in the migration/precipitation balance.
Extrusion & Post slip masterbatchinsufficient slipPE blown filmmigrationCOF
1 görüntüleme
Tam Yanıtı Oku →