ABS brittle cracking——metal insert stress
Problembeschreibung
ABS products with metal inserts show cracks around the insert.
Ursachenanalyse
The thermal expansion/shrinkage rates of ABS and metal differ greatly; during cooling shrinkage, circumferential tensile stress is generated at the insert interface; it is more severe when the insert is not preheated.
Lösung
①Minimize metal inserts; ②when they must be used, preheat the insert to near the mold temperature; ③ensure sufficient wall thickness around the insert and set rounded transitions; ④appropriately increase the mold temperature to slow the shrinkage difference.
Wichtigste Erkenntnis
Insert parts need preheating, and sufficient interface wall thickness must be reserved.