PPO Secondary Processing Cracks
Problembeschreibung
[Problem Phenomenon] Cracks appear after machining and ultrasonic welding of PPO products
Ursachenanalyse
Residual stress releases and cracks under the energy input of secondary processing; PPO can be secondarily processed but parts with internal stress are at high risk; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
Lösung
Anneal to relieve stress before secondary processing; sharp tools and low feed for machining; optimize ultrasonic welding parameters to reduce stress; after adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
Wichtigste Erkenntnis
Anneal before PPO secondary processing; energy input will awaken residual stress; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
War das hilfreich?
0 Personen fanden dies hilfreich
Vielen Dank für Ihr Feedback!