CMC and filler interface bonding poor
Problembeschreibung
The tensile strength of the CMC and filler composite material is instead lower than that of pure CMC, playing a negative role
Ursachenanalyse
The interface affinity between the filler and CMC is poor and no coupling agent treatment is used; the filler particles agglomerate and the dispersion particle size is >5μm; the wettability of CMC to the rigid filler is insufficient
Lösung
1) Filler pretreatment with silane coupling agent KH-560 0.5-1wt%; 2) Add CMC compatibilizer 2-3wt% to strengthen the interface bonding; 3) Use ultrafine filler d50<2μm; 4) Twin-screw high-shear blending to ensure dispersion
Wichtigste Erkenntnis
The interface between the elastomer and the filler requires the dual action of coupling agent and compatibilizer, otherwise the filler has a negative effect