Problem & Lösung

Praktische Antworten auf häufige Herausforderungen mit Kunststoffmaterialien

Artikel durchsuchen →

Q

PLA Narrow Processing Window

A

PLA's narrow window is the material's nature; parameter discipline and equipment precision are the double insurance for stable production; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; narrow window; brittleness; thermal stability; humidity

Q

Undried PLA Runs Better Instead

A

The undried illusion of PLA is a classic trap; improved flowability precisely indicates that the molecular weight has been destroyed by hydrolysis; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; undried illusion; hydrolytic viscosity reduction; dark halo

Q

Five Mechanisms of PLA Thermal Degradation

A

PLA degradation is multi-mechanism superposition; joint control of the three variables humidity, temperature and residence, and monitoring the melt index to quantify degradation; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; thermal degradation; depolymerization; transesterification; lactic acid

Q

PLA Anti-rehumidification After Drying

A

PLA anti-rehumidification requires accounting for the increment; direct connection plus nitrogen sealing makes the 5ppm increment the design index of the feeding system; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; rehumidification; nitrogen sealing; direct connection; 5ppm

Q

PLA Deep Dehumidification 85℃

A

Drying for high-requirement PLA processing is system engineering; dew point -55℃ plus 4 hours of residence is the equipment guarantee for ppm-level moisture; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; deep dehumidification; 85℃; -55℃; 30ppm

Q

PLA Pre-crystallization Anti-sticking

A

Pre-crystallization is the pre-process of PLA drying; the 78℃ stepped heating method saves 22% energy compared with the constant temperature method and prevents sticking; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; pre-crystallization; 78℃; stepped heating; anti-sticking

Q

PLA Drying Temperature 80-90℃

A

PLA drying temperature depends on the crystallization state; low-temperature pre-crystallization before crystallization is the iron rule to prevent sticking and tower blockage; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; drying temperature; pre-crystallization; sticking; 45℃

Q

PLA High-Temperature Processing 50ppm

A

PLA's moisture red line tightens with temperature; processes above 240℃ must implement 50ppm-level ultra-strict drying; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; 50ppm; 240℃; residence; high temperature

Q

PLA Drying 0.01% Red Line

A

100ppm is the golden red line for PLA processing; hydrolytic viscosity reduction is irreversible, and drying must be quantified to the ppm level rather than based on experience; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Material Drying PLA; drying; 100ppm; hydrolysis; dew point -40℃

Q

Storage Management of PLA Products

A

PLA storage period management is strict; sealing and turnover are the keys.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future

Material Drying PLA; storage; moisture absorption; degradation; sealing; turnover