Problem & Lösung

Praktische Antworten auf häufige Herausforderungen mit Kunststoffmaterialien

Artikel durchsuchen →

Q

ABS melt temperature upper limit 280°C

A

ABS melt temperature 280°C is the decomposition red line, discoloration is an alarm; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar prob...

Processing Machinery melt temperature 280°C thermal decomposition black speck

Q

ABS barrel zone temperature

A

ABS barrel progressive temperature increase, nozzle slightly lower to prevent drooling; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar p...

Processing Machinery barrel zoning progressive nozzle plasticization

Q

ABS transparent grade processing

A

The fine process of ABS transparent grade is optical quality; surface and inspection both emphasized; prevention and control ensures transparency.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Processing Machinery ABS; transparent grade; MABS; transparency; toughness; optics

Q

ABS impact-resistant grade processing

A

The rubber phase protection of ABS impact-resistant grade is the core; shear and temperature management; verification ensures toughness.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Processing Machinery ABS; impact-resistant grade; toughness; rubber phase; shear heat; low temperature

Q

ABS vent 0.025-0.05

A

The depth and position of ABS vents are standards; ends and weld lines are key points; maintenance ensures long-term effectiveness.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Processing Machinery ABS; vent; 0.025-0.05mm; end; weld line; burnt

Q

ABS wall thickness 1.5-3.5mm

A

ABS uniform wall thickness and gradual transition are the design foundation; sink marks and stress are the main risks; specifications ensure quality.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Processing Machinery ABS; wall thickness; 1.5-3.5mm; uniform; gradual; sink mark

Q

ABS back pressure 5-15MPa

A

The coordination of ABS back pressure and screw speed is plasticization quality; shear heat management protects the rubber phase; actual measurement prevents deviation.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Processing Machinery ABS; back pressure; 5-15MPa; screw; 40-70rpm; shear heat

Q

ABS barrel temperature gradient

A

ABS barrel gradient is fine temperature control; nozzle slightly lower to prevent drooling; verification ensures plasticization quality.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence

Processing Machinery ABS; barrel temperature; gradient; nozzle; 200-230°C; drooling

Q

ABS brittle cracking——improper screw plasticizing parameters

A

ABS screw parameters should be 'moderate': the speed and back pressure are not the higher the better, shear heat is an invisible degradation source; using the actual melt state as the criterion is more reliable than memorizing the parameter table.

Processing Machinery ABS；brittle cracking；screw speed；back pressure；shear heat

Q

ABS brittle cracking——unreasonable temperature parameters

A

ABS temperature is a 'double-edged sword': too low causes under-plasticization brittleness, too high causes degradation brittleness; set the range according to the grade, adjust the rear section according to the regrind, and judge by the melt state rather than the displayed temperature, only then...

Processing Machinery ABS；brittle cracking；melt temperature；plasticizing；degradation；temperature window