Problem & Lösung

Praktische Antworten auf häufige Herausforderungen mit Kunststoffmaterialien

Artikel durchsuchen →

Q

LLDPE blown film bubble breakage

A

Bubble breakage is the main constraint on increasing the LLDPE proportion; blending modification balances performance and stability better than reducing output.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence.

Extrusion & Post LLDPE; blown film; bubble breakage; melt strength; LDPE; blow-up ratio

Q

LLDPE blown film high extrusion pressure

A

LLDPE processing pressure management relates to energy consumption and equipment life; PPA can reduce consumption by 30~60% while improving surface quality.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence.

Extrusion & Post LLDPE; blown film; extrusion pressure; torque; PPA; energy consumption

Q

LLDPE blown film die lip buildup

A

Die lip buildup is a persistent problem in LLDPE production; PPA lubricating layer technology can significantly extend the die cleaning cycle.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence.

Extrusion & Post LLDPE; blown film; die lip buildup; PPA; lubrication; die cleaning

Q

LLDPE blown film gel particles

A

LLDPE has higher requirements on screw plasticization capability than LDPE; equipment upgrading and enhanced filtration are the core of gel particle control.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence.

Extrusion & Post LLDPE; blown film; gel particles; gel; screw; screen

Q

LLDPE blown film sharkskin melt fracture

A

LLDPE is a high-incidence material for sharkskin; PPA aid can quickly eliminate it without modifying equipment, and works better with a wide die gap.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence.

Extrusion & Post LLDPE; blown film; sharkskin; melt fracture; PPA; die exit

Q

LLDPE blown film bubble instability

A

LLDPE bubble stability is inherently weaker than LDPE; blending LDPE is the most common improvement method, and combining with cooling and bubble stabilizing devices gives better results.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurr...

Extrusion & Post LLDPE; blown film; bubble instability; melt strength; LDPE blending; bubble stabilizer

Q

LLDPE injection molded product short shot

A

For short shots, first increase speed and check venting.

Injection Molding LLDPE; '2079851475616104452; short shot; venting; gate

Q

LLDPE film water cooling ring marks

A

Ring marks = periodic uneven cooling.

Molding Process LLDPE; film; ring marks; cooling; air ring

Q

LLDPE film yellowing during storage

A

Yellowing = aging.

Material Analysis LLDPE; film; yellowing; aging; storage

Q

LLDPE injection molded product surface mottling

A

Mottling = unstable melt front.

Injection Molding LLDPE; '2079851475616104452; uneven gloss; mold temperature; melt front