문제 현상
Ejection whitening marks appear at the ejection position of ASA products, ejection cracking occurs at deep cavity reinforcing ribs, and it still occurs intermittently after ejection system adjustment.
원인 분석
Local product temperature is too high and stiffness insufficient during ejection; ejector pin pressure concentration exceeds the material bearing limit; insufficient demolding draft and poor cavity polishing increase the clamping force; excessive holding pressure aggravates mold sticking.
해결 방법
①Reduce holding pressure and fully cool before ejection; ②increase ejector pin number and area to disperse pressure; ③check demolding draft and cavity polishing; ④rounded corner transition at rib roots reduces stress concentration.
핵심 요약
ASA ejection whitening and cracking is a balance problem of pressure, temperature and friction; excessive holding pressure is an often overlooked cause; ejection system design should be synchronized with product review.
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!