문제 현상
【Problem Phenomenon】ASA printed parts have weak interlayer bonding, cracking along layers under force
원인 분석
Low extrusion temperature and too fast cooling cause insufficient interlayer diffusion; low chamber temperature and large interlayer temperature difference, poor fusion; during on-site troubleshooting, verify item by item according to this mechanism, avoid blindly adjusting the machine based only on experience
해결 방법
Increase nozzle temperature to window upper limit; enclosed chamber for heat preservation; fan 0% to reduce interlayer cooling; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability
핵심 요약
ASA printing weak interlayer first raise temperature, chamber heat preservation and fan off; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!