Injection Molding
7 조회수
COC Short Shot Insufficient Filling
문제 현상
COC products thin-wall areas and flow ends are incompletely filled, material shortage edges are rounded, microstructure replication incomplete, still unstable after raising temperature.
원인 분석
COC melt viscosity is sensitive to temperature, fluidity is insufficient to complete long-flow filling when temperature is low; too slow injection speed cools the front; poor venting forms air back pressure hindering end filling.
해결 방법
①Raise melt temperature to the upper limit of the recommended range according to grade; ②injection speed adopts medium-high speed 50~150mm/s; ③strengthen end venting; ④check shot weight and runner gate size matching.
핵심 요약
COC short shot treatment first temperature then speed then venting; medium-high speed filling is the officially recommended process; microstructure parts need special verification of replication integrity.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!