Injection Molding
5 조회수
COC Obvious Weld Lines
문제 현상
In COC transparent parts the weld line visibility is high, the strength at the confluence of multi-gate parts is low, cracking occurs along the weld line under stress, and optical uniformity is impaired.
원인 분석
When two melt fronts converge, the temperature drops, and the interfacial entanglement of amorphous COC depends on temperature; low mold temperature and insufficient injection speed cause the fronts to cool too much; poor venting aggravates interfacial weakening.
해결 방법
①Increase mold temperature and melt temperature, fill at medium-high speed to maintain front temperature; ②strengthen venting in the confluence area; ③optimize gate layout to move the weld line out of the optical zone and stressed zone; ④use a single-gate scheme if necessary.
핵심 요약
COC weld lines have nowhere to hide on transparent parts; the gate scheme can cure the problem more radically than process adjustment; weld line planning for optical parts should be completed at the mold design stage.; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!