Molds & Tooling
4 조회수
LCP Warpage and Anisotropic Shrinkage
문제 현상
【Problem Phenomenon】Flat-plate or frame-shaped LCP products warp and deform after demolding; the shrinkage rates differ greatly between the flow direction and the perpendicular direction, and dimensions are inconsistent in the two directions
원인 분석
LCP rigid molecular chains orient along the flow direction, with extremely small longitudinal shrinkage and large transverse shrinkage; shrinkage anisotropy causes internal stress warpage; the Celanese guide points out that mineral filling can reduce the anisotropy ratio to nearly 1
해결 방법
For warpage-sensitive products, select mineral or glass-mineral hybrid filled grades; optimize gate position and number to make orientation symmetric; keep mold temperature uniform and extend holding and cooling, and use a sizing fixture for correction if necessary
핵심 요약
Anisotropy is the root cause of LCP warpage; selecting a mineral-filled grade plus symmetric orientation is most effective; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!