Poor Interfacial Bonding in LCP Insert Molding
문제 현상
【Problem Phenomenon】After '2079851475616104452 LCP onto metal inserts, the interfacial bonding force is insufficient, and they detach in torsion-tension tests
원인 분석
LCP has extremely small shrinkage and is chemically inert, so its gripping force on metal and interfacial bonding are weak; when insert preheating is insufficient, the melt at the contact surface quenches and bonding is even worse; during on-site troubleshooting, verify item by item according to this mechanism to avoid blindly adjusting the machine based solely on experience
해결 방법
Preheat inserts to near mold temperature before molding; knurl the metal surface or design structural locks to provide mechanical anchoring; include interfacial bonding force verification in first article inspection; after adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
핵심 요약
LCP's low shrinkage gives weak gripping on inserts; preheating plus mechanical anchoring is double insurance; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!