LLDPE blown film machine-direction strength
문제 현상
Film machine-direction tensile strength is insufficient, tearing along the machine direction during packaging use
원인 분석
Too small a draw ratio gives insufficient molecular orientation in the machine direction; too high melt temperature breaks molecular chains; too fast cooling rate causes uneven crystallization; LLDPE itself is stronger than LDPE but this must be realized through process
해결 방법
①Increase draw ratio to 1.5-3 times to enhance orientation; ②lower barrel rear-zone temperature to prevent degradation; ③adjust frost line to optimize cooling gradient; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
LLDPE machine-direction strength is pulled by the draw ratio; the 1.5-3 times orientation range plus temperature protection is needed to realize the performance advantage; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!