문제 현상
【Problem phenomenon】SLS printed PA12 parts had many internal pores, with density and strength not up to standard
원인 분석
Dampened material or insufficient preheating leads to pores: powder moisture vaporizes into pores during laser sintering; when preheating is insufficient, melting is inadequate and gas is entrapped; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
해결 방법
Dry the powder at 80℃ for 6-8 hours before printing until the moisture content is below 0.1%; increase preheating temperature by 5-10℃; appropriately increase laser power to fully discharge internal gas
핵심 요약
For SLS pores, first dry the powder and then raise preheating, with laser power assisting gas discharge; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!