Injection Molding
6 조회수
PA6 '2079851475616104452 flash
문제 현상
Thin flake flash at the parting line and ejector pins, needs trimming after demolding, more obvious in individual cavities of multi-cavity molds.
원인 분석
PA6 melt viscosity is low and easily seeps into fitting gaps under high pressure; high injection pressure, insufficient clamping, and mold wear all induce it; low viscosity is the material root cause of PA6 flash.
해결 방법
①Reduce injection and holding pressure, lowering by 5%~10% each time while observing; ②calculate whether the clamping force is sufficient based on the projected area of the product; ③repair the fitting gaps of the parting line and ejector pins; ④appropriately lower the melt temperature to increase melt viscosity; ⑤troubleshoot filling imbalance in multi-cavity molds.
핵심 요약
PA6 flash='low viscosity meets pressure and gaps': reducing pressure is the first choice, repairing fits is fundamental; nylon melt is thin and extremely sensitive to both pressure and gaps, so process and mold must be addressed on both fronts.
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!