PA66 barrel temperature zoning
문제 현상
PA66 poor plasticizing entrains unmelted particles, local product strength low
원인 분석
Barrel temperature gradient set unreasonably; when compression zone temperature is insufficient, material not fully molten enters the metering zone, screw shear insufficient to remedy; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based solely on experience
해결 방법
Barrel gradient set as rear 260℃, middle 275℃, front 285℃; back pressure 0.5-1.0MPa to strengthen plasticizing; regularly check screw wear
핵심 요약
Reasonable temperature gradient plus appropriate back pressure is the guarantee of PA66 plasticizing quality; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems