Molds & Tooling
3 조회수
PA66 suck-back anti-drool setting
문제 현상
PA66 melt flows intermittently from the nozzle between molding cycles, contaminating the mold parting line
원인 분석
PA66 melt viscosity is low and fluidity good, barrel residual pressure pushes melt out of the nozzle, drooled material oxidizes and mixes into products forming defects; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based solely on experience
해결 방법
Set suck-back pull 3-5mm to release pressure; nozzle uses needle valve self-locking type; drooled material cleaned promptly, must not remain on the parting line; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
Low-viscosity melt anti-drool relies on suck-back plus self-locking nozzle combination; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!