PA66 weld line strength
문제 현상
PA66 structural parts break along weld lines, with strength only half of the base material
원인 분석
The two melt flow fronts have low temperature and entrap gas, and molecular entanglement at the convergence is poor; PA66's rapid solidification aggravates weld line weakening; during on-site troubleshooting, verify item by item according to this mechanism, avoiding blindly adjusting the machine based only on experience
해결 방법
Raise melt temperature and mold temperature; open venting and overflow wells at weld lines; adjust gates to avoid stressed areas; change load-bearing parts to single-point gating; after adjustment, take continuous samples to verify the effect, confirm stability before resuming mass production
핵심 요약
Weld lines rely on process strengthening plus structural avoidance, load-bearing parts are solved from the gating scheme; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence; include this case in the defect archive as a troubleshooting reference for subsequent similar problems
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!