Material Drying
4 조회수
PA6 Drying 0.2% Red Line
문제 현상
PA6 products show silver streaks and bubbles, impact strength decreases, and the fracture surface becomes brittle and spongy
원인 분석
The amide groups of PA6 are highly polar and extremely hygroscopic, with an equilibrium water absorption rate of 2.8% in a 50%RH environment; residual moisture vaporizes in the 240-270°C melt and hydrolyzes the amide bonds, causing an irreversible decrease in molecular weight
해결 방법
①Dehumidifying drying at 80-100°C for 4-8 hours, reducing the moisture content below 0.2%; ②use immediately after drying, re-drying is required if exposed to air for more than 30 minutes; ③verify by actual measurement with the Karl Fischer method
핵심 요약
0.2% moisture content is the lifeline of PA6 processing; hydrolysis damage is irreversible and difficult to detect by appearance, so drying must be quantified by actual measurement rather than estimated by experience; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!