Material Drying
6 조회수
PA6 Radiator Tank
문제 현상
The radiator plastic tank cracks and leaks after long-term use in coolant
원인 분석
The tank contacts high-temperature antifreeze for a long time, PA6 hydrolysis and glass fiber interface erosion cause strength decay, and stress concentration at the welded rib cracks first; when troubleshooting on site, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
해결 방법
Select hydrolysis-resistant glass-fiber reinforced PA6 dedicated grades; optimize the welded rib structure to avoid stress concentration; verify by long-term immersion test in 135°C coolant; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability
핵심 요약
Coolant contact parts must use hydrolysis-resistant grades plus long-term medium verification; after confirming effectiveness, fix the parameters and practices into the work instructions to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!