Molding Process
4 조회수
PA6 Weld Line Strength
문제 현상
Strength at the weld line is obviously insufficient, and snap-fits and tensile parts break along the weld line
원인 분석
When PA6 melt fronts meet, the surface solidified film hinders molecular chain entanglement, making the weld line a weak strength zone; glass fibers orient perpendicularly at the weld line, further weakening the bonding strength
해결 방법
①Raise melt and mold temperatures to improve the meeting quality; ②Arrange gates so the weld line avoids load-bearing areas; ③Set overflow wells at the weld line to discharge the cold material front; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
The PA6 weld line is a required question of structural design; position transfer takes priority over process remedy, and load-bearing areas must stay away from weld lines; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!