PA6 Hot Oil Aging
문제 현상
After long-term use, PA6 engine compartment parts show surface cracking and strength decline
원인 분석
High temperature and engine oil medium jointly accelerate PA6 oxidative degradation, and additives in hot oil may also cause chemical attack, with aging expanding from the surface layer to the interior; during on-site troubleshooting, verify item by item according to this mechanism, avoiding blind machine adjustment based only on experience
해결 방법
Select heat-aging-resistant grades (containing heat stabilizer systems) for engine compartment parts; periodically perform hot oil aging verification according to standards; replace parts with surface cracking in time to prevent fracture failure
핵심 요약
For hot oil environments, heat-stabilized grades must be selected and aging verification performed; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!