PBT Draft Angle and Forced Demolding
문제 현상
The product is scratched during demolding, or forced demolding of pure PBT parts with undercut structures fails
원인 분석
Pure PBT can reach an elongation of 200%, and smaller undercuts can be forcibly demolded; but after glass fiber filling, the elongation drops greatly and forced demolding is not possible; the core draft angle must be at least 0.5°
해결 방법
①Core draft angle ≥0.5°, main runner draft ≥3°; ②Pure material with small undercuts can be forcibly demolded; ③Forced demolding is forbidden for glass fiber filled parts; after adjustment, take samples continuously to verify the effect, and resume mass production only after confirming stability
핵심 요약
PBT demolding design is differentiated according to whether it is filled or not; the forced demolding capability of pure material no longer exists in glass fiber grades; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!