Injection Molding
6 조회수
PC Short Shot Caused by High Viscosity
문제 현상
Thin-wall or long-flow PC products cannot be filled, the short-shot edges are rounded, it recurs at the same position, and improvement after raising pressure is limited.
원인 분석
PC melt viscosity is much higher than general-purpose plastics, and flow resistance is large; low melt temperature, insufficient injection pressure/speed, and too small a gate all amplify filling difficulty; the thin-wall long-flow structure itself is a challenge for high-viscosity materials.
해결 방법
①Raise the melt temperature to near the recommended upper limit (not exceeding the degradation temperature) to reduce viscosity; ②Increase injection pressure and speed; ③Enlarge the gate and runner and shorten the flow length; ④Increase the mold temperature to delay solidification; ⑤Select high-flow grades when necessary.
핵심 요약
For PC short shot, first 'raise temperature and speed up', then 'large gate', and finally 'change grade': high viscosity is PC's nature; when the structure allows, shortening the flow length and enlarging the gate is more effective than forcibly raising pressure, and also better protects the mold.
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!