Injection Molding
6 조회수
PCL High Melt Viscosity and Difficult Filling
문제 현상
PCL '2079851475616104452 filling is incomplete, with short shots at thin walls and long flow paths, still difficult even with high pressure and high speed.
원인 분석
PCL melt phase has high viscosity and poor flow; higher temperature is needed to reduce viscosity but there is degradation risk; high molecular weight aggravates it; runner and gate resistance.; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
해결 방법
①Appropriately increase melt temperature to 140~180°C; ②optimize injection pressure and speed; ③enlarge runner and gate sizes; ④select molecular weight grades; ⑤increase mold temperature.
핵심 요약
PCL high viscosity is the main processing challenge; temperature and structure are equally important; molecular weight selection affects processability.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!