PC metal insert preheating
문제 현상
【Problem Phenomenon】PC metal insert cracking after molding
원인 분석
PC and metal have large differences in thermal expansion coefficient; when inserts are not preheated, the melt encounters cold metal and shrinks rapidly causing cracking; preheating inserts to 100-120℃ reduces stress；During on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based solely on experience
해결 방법
Insert preheating 100-120℃; design fillets to reduce stress concentration; annealing to eliminate stress；After adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
핵심 요약
PC inserts must be preheated to 100-120℃, cold and hot meeting causes cracking；After confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence；Include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!