PE Product ESCR Environmental Stress Cracking
문제 현상
After contacting detergents, oils and industrial chemicals, HDPE containers and pipes develop brittle microcracks after a period of use, cracking without swelling or stretching.
원인 분석
PE undergoes environmental stress cracking under the combined action of internal or external mechanical stress and chemical media (surfactants, alcohols, oils, detergents); HDPE, due to its linear molecular chains and high crystallinity, is more prone than LLDPE; areas with high internal stress fail first.
해결 방법
①Select ESCR-resistant grades according to the media (high molecular weight, narrow molecular weight distribution HDPE, or introducing mLLDPE blending to absorb local stress); ②reduce the product internal stress (optimize holding, cooling, eliminate sharp corners); ③conduct media immersion/ESCR verification; ④avoid interference fit assembly and sharp corners.
핵심 요약
ESCR is the most common cause of 'premature death' of durable PE products: material grade, internal stress and media must superimpose to cause failure; blow molded household chemical bottles and industrial drainage pipes are disaster areas, and material selection and verification must be moved upstream.
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!