Extrusion & Post
11 조회수
The Trade-Off of 300℃ High-Temperature Annealing of PEEK
문제 현상
[Problem Phenomenon] After 300℃ annealing in pursuit of ultimate performance, PEEK parts become brittle and the surface oxidizes and discolors
원인 분석
Annealing near 300℃ can maximize strength, modulus, and chemical resistance, but is accompanied by embrittlement and surface oxidation; large-diameter parts (>6.3cm) also require 300℃ annealing for several hours when the core-surface crystallization rate difference triggers internal stress cracking
해결 방법
Ultimate-performance parts may use 300℃ annealing but the embrittlement cost must be evaluated; anneal large parts to prevent crystallization stress cracking; select the annealing atmosphere and surface protection according to service requirements
핵심 요약
300℃ annealing is a performance-limit means, and the embrittlement and oxidation costs must be evaluated in advance; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence