PEEK Compression Molding Pores and Bubbles
문제 현상
【Problem Phenomenon】PEEK compression molded products have many internal pores and bubbles, and the density does not meet the standard
원인 분석
Air entrapment in the powder and insufficient drying are the main causes of pores; the Victrex compression molding procedure requires 450PF fine powder to be pre-dried at 150℃×3h or 120℃ overnight, and the mold must also be pre-dried at 150℃
해결 방법
Fully pre-dry the powder and control the material layer thickness; pre-dry the mold to remove moisture; pre-press at 350-700bar to vent air before heating up to melt; after adjustment, continuously sample to verify the effect, and resume mass production after confirming stability
핵심 요약
Compression molding pores are controlled by double drying (material + mold) plus pre-pressing venting; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a troubleshooting reference for similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!