Improper PEI Drying Temperature
문제 현상
When drying PEI, too low a temperature does not remove water thoroughly, and too high a temperature (>160℃) causes surface pre-crosslinking; both ends produce processing defects.
원인 분석
The PEI drying temperature window has bidirectional constraints: below 110℃ water cannot be effectively removed, and above 160℃ surface pre-crosslinking easily occurs; the base grade ULTEM 1000 uses 120~130℃, and glass fiber reinforced grades need to be increased to 130~150℃ due to poor thermal conductivity.
해결 방법
①Select the drying temperature by grade: base grade 120~130℃, reinforced grade 130~150℃; ②strictly prohibit exceeding 160℃ to prevent pre-crosslinking; ③use a dehumidifying dryer to avoid secondary moisture absorption of ordinary ovens; ④adjust the drying time of 4~8 hours according to verification.
핵심 요약
PEI drying temperature is narrow-window management; pre-crosslinking is a specific failure of excessive high temperature; grade-differentiated settings cannot be one-size-fits-all.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!