Extrusion & Post
11 조회수
POM internal stress cracking and embrittlement
문제 현상
Cracks appear in products after a period of use, starting first at assembled stressed parts, improving after annealing or reducing injection pressure.
원인 분석
Excessive injection pressure and too low mold temperature cause large internal stress in products; POM crystalline material releases internal stress slowly and cracks along stress concentration points when stressed or in contact with media.
해결 방법
①Reduce injection and holding pressure; ②increase mold temperature; ③extend cooling time for slow shaping; ④perform annealing to release stress if necessary.; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
Internal stress cracking has a lag and is difficult to detect at the factory; a mild process with low pressure and high mold temperature is the prevention principle, and critical parts should undergo stress verification.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!