PPO Thin-Wall Delamination
문제 현상
[Problem Phenomenon] Delamination and peeling of PPO thin-walled parts, cracking along the layer plane when bent
원인 분석
When mold temperature is below 100°C, thin-walled plastic parts are prone to insufficient filling and delamination; the frozen layer of the melt front bonds poorly with the subsequent melt, forming a weak interlayer interface; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
해결 방법
Raise the mold temperature above 100°C to improve thin-wall filling and interlayer bonding; raise melt temperature and injection speed; arrange gates close to thin-wall areas; after adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
핵심 요약
PPO thin-wall delamination is a signal of insufficient mold temperature, with high risk below 100°C; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!