문제 현상
[Problem Phenomenon] PPO products pass factory inspection but crack after assembly or a period of use
원인 분석
Residual internal stress is released with delay and cracks under load, temperature or media; stress relaxation and creep redistribute assembly stress; during on-site troubleshooting, verify item by item according to this mechanism, and avoid blindly adjusting the machine based only on experience
해결 방법
Anneal high-stress parts after molding; design assembly torque and interference according to the material's creep characteristics; perform fracture analysis on failed parts to locate the stress source; after adjustment, take continuous samples to verify the effect, and resume mass production only after confirming stability
핵심 요약
PPO delayed cracking is a residual stress debt; annealing plus assembly design prevents it; after confirming effectiveness, solidify the parameters and practices into the work instruction to prevent recurrence; include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!