문제 현상
Transparent PS products crack upon demolding or slight force, and cracks mostly start at corners, rib positions or weld lines.
원인 분석
Material overheating or over-shearing reduces molecular weight and makes it brittle; improper molding conditions produce high internal stress, and one-sided rapid cooling causes stress differences, all of which make GPPS brittle and crack.
해결 방법
①Check barrel temperature to prevent overheating degradation; ②optimize molding conditions to reduce internal stress; ③balance cooling to avoid one-sided rapid cooling; ④when cracking occurs at weld lines, move the gate to change the filling pattern.
핵심 요약
GPPS brittle cracking should be investigated along two lines: material degradation and internal stress; transparent parts can use polarizers to observe stress distribution to assist positioning.; after confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!