Injection Molding
4 조회수
PSU Melt Fracture and Mold Filling Difficulty
문제 현상
When PSU is filled at increased injection speed, melt fracture appears on the product surface; the speed limit causes mold filling difficulty, and the contradiction is prominent for thin-walled long-flow parts.
원인 분석
PSU melt viscosity remains very high; excessive injection speed causes melt fracture, limiting the filling speed; the critical shear rate restricts the possibility of high-speed filling.
해결 방법
①Control injection speed in the medium range to avoid melt fracture; ②Increase melt temperature to reduce viscosity and assist filling; ③Optimize runners and gates to reduce flow resistance; ④Wall thickness not less than 1.5mm to ensure the flow length ratio.
핵심 요약
PSU filling speed is limited by the melt fracture ceiling; temperature and structural compensation are more effective than forcibly increasing speed; a flow length ratio of 80 is a design constraint.; After confirming effectiveness, solidify the parameters and practices into the work instructions to prevent recurrence
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!