PSU Characteristic of Hard-to-eliminate Internal Stress
문제 현상
[Problem Phenomenon] PSU products crack after storage; environmental stress cracking test failed
원인 분석
PSU melt cools fast and molecular chains are rigid; molding internal stress is difficult to eliminate by itself; residual stress releases and cracks under solvent or load; During on-site troubleshooting, verify item by item according to this mechanism, avoiding blindly adjusting the machine based solely on experience
해결 방법
After molding, use hot molds and full annealing to reduce internal stress; avoid contact with polar solvents; for high-stress-risk parts, perform post-annealing solvent immersion verification; after adjustment, continuously sample to verify the effect, and resume mass production only after confirming stability
핵심 요약
PSU internal stress is inherently hard to eliminate; hot mold plus annealing are standard procedures; After confirming effectiveness, solidify the parameters and practices into the work instructions to prevent recurrence; Include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!