Extrusion & Post
11 조회수
PVDF Annealing to Eliminate Internal Stress
문제 현상
【Problem phenomenon】PVDF precision parts show dimensional drift after storage and crack during assembly, more obvious in machined parts
원인 분석
Internal stress introduced by molding and machining is slowly released during storage, causing dimensional changes and stress cracking; CS-Seal recommends 100℃×2h stress relief annealing for precision parts after machining, and 80-120℃ annealing for sheets and rods
해결 방법
Anneal precision parts at 100℃×2h after machining; anneal injection-molded sheets and rods at 80-120℃ to stabilize dimensions; cool slowly after annealing to prevent new stress; re-measure critical dimensions after annealing
핵심 요약
Annealing is the last guarantee of dimensional stability for PVDF precision parts; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; Include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!