PVDF Fluoropolymer Foam Extrusion
문제 현상
【Problem phenomenon】PVDF foamed cable extrusion shows uneven foaming and cell collapse, making weight reduction and performance hard to achieve together
원인 분석
The matching of blowing agent decomposition temperature and melt temperature, nucleation uniformity, and melt strength jointly determine cell quality; Arkema 2620 FC foaming masterbatch is specially designed for PVDF continuous extrusion to stabilize foaming
해결 방법
Select Kynar 2620 FC special foaming masterbatch and follow the recommended ratio; precisely match the foaming zone temperature to the blowing agent decomposition window; verify the balance between the weight reduction extent and mechanical property retention
핵심 요약
PVDF foaming relies on special masterbatch and temperature window matching to stabilize cells; After confirming effectiveness, fix the parameters and practices into the work instruction to prevent recurrence; Include this case in the defect archive as a reference for troubleshooting similar problems in the future
이 정보가 도움이 되었나요?
0 명이 도움이 되었다고 합니다
의견 주셔서 감사합니다!