문제 현상
EVOH film heat shrinkage rate at 80°C >12%, exceeding the 5% dimensional stability requirement
원인 분석
EVOH extrusion orientation released after heating causing large shrinkage; EVOH thermal expansion coefficient large; film cooling froze a large amount of orientation stress
해결 방법
1) Reduce extrusion draw ratio to reduce orientation freezing; 2) Film annealing treatment at 60-80°C to release orientation stress; 3) Add 5-10wt% rigid resin to reduce heat shrinkage rate; 4) Biaxial stretching process to balance orientation
핵심 요약
Film heat shrinkage is caused by orientation freezing; reducing draw ratio and annealing treatment are key