Large EVOH Compression Set
문제 현상
EVOH product compression set >30%, failing the 15% requirement
원인 분석
EVOH elastic recovery insufficient; crosslinking degree too low, plastic deformation unrecoverable; density too low, cell walls thin, recovery poor
해결 방법
1) Increase crosslinking degree to 60-70% to reduce plastic deformation; 2) Select high elastic recovery EVOH grade; 3) Add reinforcing filler
핵심 요약
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key