Low PVA elongation at break
문제 현상
PVA product elongation at break <100%, below the 200% requirement
원인 분석
PVA molecular weight on the low side, short chains, insufficient entanglement; excessive orientation, extremely low transverse elongation; excessive crosslinking limiting chain slippage
해결 방법
1) Select high molecular weight PVA to increase entanglement density; 2) Reduce orientation, lower injection speed; 3) Control crosslinking degree to avoid excess
핵심 요약
Low elongation at break is caused by low molecular weight and orientation; selecting high MW and reducing orientation are the key