Cracking, deformation, or poor coating occurs during secondary processing
문제 현상
Cracking, deformation, or poor coating occurs during secondary processing
원인 분석
Cracking during machining (PA has high dry-state brittleness)
Insufficient surface treatment before coating, poor coating adhesion
Local overheating and degradation during hot bending or welding
Improper ultrasonic welding energy, poor weld quality
Poor compatibility between ink and cellulose acetate butyrate during printing, peeling off
해결 방법
Conditioning treatment before machining to reduce brittleness
Full surface treatment before coating (grinding/primer)
Control secondary heating temperature to avoid degradation
Optimize ultrasonic welding parameters
Select ink compatible with cellulose acetate butyrate
핵심 요약
Post-processing needs to consider material state and compatibility