Injection Molding
5 조회수
CEF '2079851475616104452 demolding difficulty
문제 현상
CEF injection molded products have large demolding force, product deformation or strain damage, demolding time accounts for 30% of the cycle
원인 분석
CEF has large adhesion to the mold cavity; insufficient draft angle <0.5°; insufficient cooling time, product demolded before fully solidified; unreasonable ejection mechanism design
해결 방법
1) Increase the mold draft angle to 1-2°; 2) Extend cooling time so the product is fully solidified before demolding; 3) Polish the mold surface to Ra<0.2μm; 4) Increase the ejection area, use a large-area ejector plate; 5) Spray release agent (temporary solution)
핵심 요약
Demolding difficulty is caused by adhesion and insufficient mold design, increasing the draft angle is the fundamental measure