CEF surface micro-cracks
문제 현상
Micro-cracks of 0.05-0.2mm appear on the surface of the CEF product, affecting the appearance and strength
원인 분석
The internal stress of the CEF product is too large, exceeding the yield stress of the material; environmental stress cracking; stress concentration in the product design
해결 방법
1) Annealing treatment to release internal stress; 2) Product design to avoid sharp corners and stress concentration; 3) Select high-molecular-weight CEF to improve crack resistance
핵심 요약
Micro-cracks are caused by excessive internal stress; annealing and crack-resistant design are the key