Material Analysis
4 조회수
Environmental Stress Cracking of Biaxially Oriented Polypropylene Film Products
문제 현상
The product cracks when it contacts a specific chemical medium while bearing stress.
원인 분석
(1) The product has residual stress, and cracking is accelerated under the action of chemical media
(2) Contact with incompatible chemical media (solvents, greases, etc.)
(3) The wall thickness of the product is uneven, and stress concentration parts are prone to cracking
(4) The molecular weight of the material is low, and the environmental stress cracking resistance is poor
(5) The service environment temperature is high, accelerating cracking
해결 방법
(1) Reduce the residual stress of the product (annealing treatment)
(2) Avoid contact with incompatible chemical media
(3) Optimize the product design with uniform wall thickness to reduce stress concentration
(4) Select a high molecular weight grade
(5) Reduce the service environment temperature
핵심 요약
Environmental stress cracking is the result of the combined action of stress and chemical media.