Insufficient long-term hydrostatic strength of linear low density polyethylene PPR pipes (Variant: strengthened measures)
문제 현상
PPR/PP-R pipes rupture in long-term hydrostatic tests (1000h, 8760h), failing to meet ISO 15874 requirements.
Insufficient long-term strength affects pipe service life and design safety factor.
In particular, additional attention is needed on the original basis; this problem is more prominent and requires key attention.
원인 분석
(1) Raw material molecular weight too low or unreasonable molecular weight distribution
(2) Improper extrusion temperature, partial material degradation
(3) Insufficient or uneven pipe wall thickness
(4) Improper cooling rate, inappropriate crystallinity
(5) Welding joints as weak points with insufficient strength
(6) On the original basis, additional attention is needed as process parameter fluctuations or equipment status changes have aggravated this problem
해결 방법
(1) Select dedicated grades meeting PPR pipe standards (MFR 0.2-0.5g/10min)
(2) Strictly control extrusion temperature at 200-220°C, avoid material degradation
(3) Ensure pipe wall thickness meets SDR value requirements and is uniform
(4) Optimize cooling conditions, ensure reasonable crystallinity (50-60%)
(5) Strengthen quality control and inspection of welding joints
(6) And strengthen process monitoring; on the original basis, additional attention is needed, with special attention to parameter stability
핵심 요약
Insufficient long-term hydrostatic strength is caused by material selection and processing quality; comprehensive control of raw material, process, and welding is needed.
Targeted preventive measures need to be taken in different production scenarios.