Processing Machinery
4 조회수
Improper processing temperature window selection for linear low-density polyethylene linear low-density polyethylene
문제 현상
Unreasonable barrel or head temperature settings lead to poor material plasticization quality, degradation or incomplete melting.
Temperature window selection directly affects melt quality and final product performance.
원인 분석
(1) Temperature setting is on the low side; high melt viscosity results in insufficient plasticization
(2) Temperature setting is on the high side; material thermal degradation reduces molecular weight
(3) Unreasonable temperature distribution across sections; feeding section temperature too high or plasticizing section temperature too low
(4) Material grade differences and MFR changes are not considered
(5) Ambient temperature changes are not adjusted in time
해결 방법
(1) Reasonably set the temperature range according to linear low-density polyethylene characteristics: 190-250°C
(2) Barrel temperature gradually increases from the feeding section to the homogenizing section, but does not exceed the upper limit temperature
(3) Regularly calibrate actual barrel temperature with a thermometer or infrared temperature gun
(4) Test MFR for each batch of raw material and fine-tune temperature as needed
(5) Establish standardized process parameter cards to reduce human operation differences
핵심 요약
Temperature window selection is the foundation of processing and needs to be reasonably set according to material characteristics and actual operating experience.